| TESTED MATERIAL |
TEST PARAMETERS |
FINDS |
|
| 01 |
AIR-O 1 |
Solvent Content |
Derivatives of Aromatic Hydrocarbons |
 |
| 02 |
AIR-O 1 |
Flash Point |
58 |
|
| 03 |
AIR-O 1 |
Content of Active Principle |
%40 Active Principle
%60 Binding Agent |
|
| 04 |
AIR-O 1 |
Freezing Point |
-20 |
|
| 05 |
AIR-O 1 |
Boiling Point |
106,5 |
|
| 06 |
AIR-O 1 |
pH at 20oC |
5,45 |
|
| 07 |
AIR-O 1 |
Specific Weight (gr/cm3) at 20oC |
0,948 |
|
| 08 |
AIR-O 1 |
Odor |
Tang odor of Aromatic Solvent |
|
| 09 |
AIR-O 1 |
Color |
No Color, Transparent, Lucid Liquid |
|
| 10 |
AIR-O 1 |
Viscosity (cp 25oC) |
6,84 |
|
| 11 |
AIR-O 1 |
Solubility (in water %) |
20 |
|
| 12 |
AIR-O 1 |
Biodegradability |
Air-O 1 is biologically degradagble to %100 in 60 days. The tests have been carried out for a variety of soil samples (Marl, topsoil etc.) |
|
| 13 |
AIR-O 1 |
Corrosion on aluminum |
Air-O 1 has no corrosive effect on aluminum
Air-O 1 does not stain aluminum |
|
| The corrison test has been carries out in our laboratories on a piece of aluminum by keeping the test material in Air-O 1 liquid for 24 hrs. |
| 14 |
Pirelli NYY 2x2,5mm Kablo TSE |
Corrison on electric cable |
No corrison has been seen on the tested material |
|
|
The corrison test has been carries out in the following steps:
- Air-O 1 has been sprayed on the tested material and left for 30 min.
- Air-O 2 has been applied to the tested material
- The tested material has been washed with water
|
| 15 |
Stenseal 2K Expansion Joint |
Corrison on expansion joint |
No corrison has been seen on the tested material |
|
The corrison test has been carries out in the following steps:
- Air-O 1 has been sprayed on the tested material and left for 30 min.
- Air-O 2 has been applied to the tested material
- The tested material has been washed with water
|
| 16 |
Piece of concrete from the runway 06 24, under seal of DHMI |
Concrete Test |
No Impairment |
|
The "concrete test" was made in compliance with the original application method given by the company as described below:
Air-O 1 was sprayed on the concrete and left to penetrate for 30 minutes. Following this application, Air-O 2 was applied to the surface and swept with water. |
| 17 |
AIR-O 2 |
Content of Active Principle |
%10 Active Principle
%90 Binding Agent |
|
| 18 |
AIR-O 2 |
Solvent Content |
Water Based |
|
| 19 |
AIR-O 2 |
Flash Point |
131 |
|
| 20 |
AIR-O 2 |
Freezing Point |
-3,5 |
|
| 21 |
AIR-O 2 |
Boiling Point |
98,5 |
|
| 22 |
AIR-O 2 |
pH (direct) at 20oC |
7,43 |
|
| 23 |
AIR-O 2 |
Specific Weight (gr/cm3) at 20oC |
1,027 |
|
| 24 |
AIR-O 2 |
Odor |
Odorless |
|
| 25 |
AIR-O 2 |
Color |
No Color, Transparent, Lucid Liquid |
|
| 26 |
AIR-O 2 |
Viscosity (cp 25oC) |
4,2 |
|
| 27 |
AIR-O 2 |
Solubility (in water %) |
100 |
|
| 28 |
AIR-O 2 |
Biodegradability |
Air-O 2 is biolagically degradable to %100 in 60 days. The tests have been carried out for a variety of soil samples (Marl, topsoil etc.) |
|
| 29 |
AIR-O 2 |
Corrosion on aluminum |
Air-O 2 has no corrosive effect on aluminum
Air-O 2 does not stain aluminum |
|
| The corrison test has been carries out in our laboratories on a piece of aluminum by keeping the test material in Air-O 1 liquid for 24 hrs. |